萊蕪 Reduced iron powders for powder metallurgy

  Chemical   composition     %

TFe
min

Mn
max

Si
max

S
max

C
max

H2-loss
max

FHY80.23

98.0

0.45

0.20

0.03

0.05

0.40

FHY80.25

98.0

0.45

0.20

0.03

0.05

0.40

FHY100.25

98.5

0.45

0.20

0.03

0.05

0.30

FHY100.27

98.5

0.45

0.20

0.03

0.05

0.25

FHY150

98.0

0.45

0.20

0.03

0.05

0.40

FHY200

98.0

0.45

0.20

0.03

0.05

0.40

Grade

       Physical   properties

Apparent density
g/cm3

Compressibility under 490Mpa
   g/cm3 min

Slow
S/50g
max

Partical size
um

FHY80.23

2.2~2.4

6.5

40

180～0

FHY80.25

2.4~2.6

6.6

35

180～0

FHY100.25

2.4~2.6

6.6

35

150～0

FHY100.27

2.6~2.8

6.7

30

150～0

FHY150

2.4~2.8

6.6

35

100～0

FHY200

2.4~2.8

6.6

35

75～0